| MAL Grade | Specification | C | Si | Mn | S | P | Cr | Ni | Mo | Condition | Size | Hardn- ess Brinell |
Tensile Strenght | Proof Strength | Elong. | Reduction in area | Impact Energy | Resis. Inter. Corro. | |
| Rm | PS(0.2%) | A | Z | ISO-V, KV | - | ||||||||||||||
| HB /BHN | '/Mpa (ksi) | '/Mpa (ksi) | % | % | J, Min | - | |||||||||||||
| HBW | - | - | - | - | - | - | |||||||||||||
| 304 | EN-10088-3:2005 | - | - | - | - | - | 18.00 | 8.00 | - | Solution | 14-80mm | 215 | 500 | 190 | 45 | 50 | 100 | - | |
| 1.4301 | 0.070 | 1 | 2 | 0.03 | 0.045 | 20.00 | 10.50 | - | Annealed | - | - | 700 | - | - | - | - | - | ||
| - | - | - | - | - | - | - | - | As Rolled | - | 230 | - | - | - | - | - | - | |||
| ASTM A276 | - | - | - | - | - | 18.00 | 8.00 | - | Solution | Up to 50.8mm | - | 650 (95) | 515 (75) | 25 | 40 | - | - | ||
| 304 | 0.080 | 1 | 2 | 0.03 | 0.045 | 20.00 | 10.00 | - | Annealed | >50.8 to 63.5 | - | 620 (90) | 450 (65) | 30 | 40 | - | - | ||
| >63.5 to 76.2 | - | 550 (80) | 380 (55) | 30 | 40 | - | - | ||||||||||||
| A 193/A 193M-07 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | ||
| Class 1& 2 | - | - | - | - | - | 18.00 | 8.00 | - | Solution | 14-80mm | 223 | '(75) 1 | '(30) | 30 | 50 | - | - | ||
| B8; S30400 | 0.080 | 1 | 2 | 0.03 | 0.045 | 20.00 | 11.00 |
- | Annealed | - | 321 | '(95) 2 | '(75) | 25 | 40 | - | - | ||
| A 182 / A 182M-07 | 0.04 | - | - | - | - | 18.00 | 8.00 | - | Solution | 14-80mm | - | 515 (75) | 205 (30) | 30 | 50 | - | - | ||
| F304 / F 304H | 0.080 | 1 | 2 | 0.03 | 0.045 | 20.00 | 10.00 | - | Annealed | - | - | - | - | - | - | - | - | ||
| 187.5/2.5- | |||||||||||||||||||
| 316 | EN-10088-3:2005 | - | - | - | - | - | 16.50 | 10.00 | 2.00 | Solution | 14-80mm | 215 | 500 | 200 | 40 | - | - | - | |
| 1.4401 | 0.070 | 1 | 2 | 0.03 | 0.045 | 18.50 | 14.00 | 2.50 | Annealed | - | - | 700 | - | - | - | - | - | ||
| ASTM A276 | - | - | - | - | - | 16.00 | 10.00 | 2.00 | Solution | <=50.8mm | - | 650 (95) | 515 (75) | 25 | 40 | - | - | ||
| 0.080 | 1 | 2 | 0.03 | 0.045 | 18.00 | 14.00 | 3.00 | Annealed | >50.8 to 63.5 | - | 620 (90) | 450 (65) | 30 | 40 | - | - | |||
| - | - | - | - | - | - | - | - | - | >63.5 to 76.2 | - | 550 (80) | 380 (55) | 30 | 40 | - | - | |||
| A 193/A 193M-07 | - | - | - | - | - | 16.00 | 10.00 | 2.00 | Solution | All | 223 | (75) | '(30) | 30 | 50 | ||||
| Class 1& 2 | 0.080 | 1 | 2 | 0.03 | 0.045 | 18.00 | 14.00 | 3.00 | Annealed | ||||||||||
| A 182 / A 182M-07 | - | - | - | - | - | 16.00 | 10.00 | 2.00 | Solution | All | 223 | (75) | '(30) | 30 | 50 | ||||
| F316 / F316H | 0.080 | 1 | 2 | 0.03 | 0.045 | 18.00 | 14.00 | 3.00 | Annealed | ||||||||||